PC-ABS is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials – the superior strength and heat resistance of PC and the flexibility of ABS. PC-ABS blends are commonly used in automotive, electronics and telecommunications applications.
Color options: Black
|Mechanical Properties1||Test Method||English||Metric|
|Tensile Strength (Type 1, 0.125”, 0.2”/min)||ASTM D638||5,900 psi||41 MPa|
|Tensile Modulus (Type 1, 0.125”, 0.2”/min)||ASTM D638||278,000 psi||1,900 MPa|
|Tensile Elongation (Type 1, 0.125”, 0.2”/min)||ASTM D638||6%||6%|
|Flexural Strength (Method 1, 0.05”/min)||ASTM D790||9,800 psi||68 MPa|
|Flexural Modulus (Method 1, 0.05”/min)||ASTM D790||280,000 psi||1,900 MPa|
|IZOD Impact, notched (Method A, 23°C)||ASTM D256||3.7 ft-lb/in||196 J/m|
|IZOD Impact, un-notched (Method A, 23°C)||ASTM D256||9 ft-lb/in||481 J/m|
|Thermal Properties2||Test Method||English||Metric|
|Heat Deflection (HDT) @ 66 psi||ASTM D648||230°F||110°C|
|Heat Deflection (HDT) @ 264 psi||ASTM D648||205°F||96°C|
|Vicat Softening Temperature||ASTM D1525||234°F||112°C|
|Glass Transition Temperature (Tg)||DMA (SSYS)||257°F||125°C|
|Coefficient of Thermal Expansion||- – - – - – - – -||4.10 E -05 in/in/°F||- – - – -|
|Melt Point||- – - – - – - – -||Not Applicable3||Not Applicable3|
|Electrical Properties4||Test Method||Value Range|
|Volume Resistivity||ASTM D257||2.0x10e14 – 4.4x10e13 ohms|
|Dielectric Constant||ASTM D150-98||2.9 – 2.7|
|Dissipation Factor||ASTM D150-98||.0035 – .0032|
|Dielectric Strength||ASTM D149-09, Method A||340 – 90 V/mil|
|Specific Gravity||ASTM D792||1.10|
|Density||ASTM D792||0.0397 lb/in3|
|Rockwell Hardness||ASTM D785||R110|
|UL File Number||—————-||E345258|
1Build orientation is on side long edge.
2Literature value unless otherwise noted.
3Due to amorphous nature, material does not display a melting point.
4All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation.
50.005 inch (0.127 mm) layer thickness not available for Fortus 900mc